AZ31B ASTM B90 magnesium alloy sheet

Magnesium plate, Grade: AZ31B, Standard: ASTM B90, Size: (T1~70mm)* (W100~1050mm) * (L600~5000mm) - details see: //www.sourcingmetals.com/az31b-astm-b90-magnesium-alloy-sheet-10191159
Place of Origin: Shaanxi China (Mainland)Brand Name: TaipuThickness: 0.5mm -30mmWidth: 100mm -1050mm
Length: 500mm -4000mmMaterial: MagnesiumGrade: AZ31, AZ61, AZ80, ZK40, ZK60,surface: bright and clean
AZ31B ASTM B90 magnesium alloy sheet
contact supplier for AZ31B ASTM B90 magnesium alloy sheet


AZ31B is a wrought magnesium base alloy with good room-temperature strength and ductility combined with corrosion resistance and weldability. Increased strength is obtained by strain hardening with a subsequent partial anneal (H24 and H26 tempers).

SIZE RANGE:

Sheet: thickness from 1mm to 6mm; Max. width is 600mm; Max. length is 6000mm;

Plate: thickness from 6 mm to 200mm; Max. width is 2800mm; Max. length is 6000mm;

Block: We can supply cut-to-size blocks according to customer's requirements.

Coil: thickness from 0.3 to 3.0mm, max. width 350mm;

APPLICATIONS

Sheet and plate in AZ31B find application in medium strength service at temperatures below 150°C. Diverse uses including aerospace, aircraft, concrete tools, 3C (cell phone / camera / computer), speaker cones and textile machinery can all benefit from light weight AZ31B.

AZ31B is non-magnetic and has high electrical and thermal conductivity filling the requirements for RFI and EMI shielding in the electronics and computer industries.

Superplastic forming of AZ31B sheet at elevated temperatures allows production of a wide variety of intricate parts for automotive uses. Monocoque construction utilizing formed sheet can be adapted to many commercial applications.

SPECIFICATIONS

ASTM B90/B90M-07; AMS 4375; AMS 4376; AMS 4377

CHEMICAL COMPOSITION

Al: 2.5-3.5%; Zn: 0.7-1.3%; Mn: 0.20 – 1.0%; Mg: Balance

PHYSICAL PROPERTIES

Density: 1.78;

Coefficient of thermal expansion: 26.8 x 10-6K-1

Specific heat: 1040 Jkg-1k-1

Thermal conductivity: 76.9Wm-1k-1

Electrical resistivity: 92nΩm

Modulus of elasticity: 45 x 109Pa;

Poissons ratio: 0.35;

Melting range: 566 - 632°C

HEAT TREATMENT

No thermal treatment is available for increasing the strength of this alloy after fabrication.

MECHANICAL PROPERTIES

Alloy and TemperThickness (mm)Yield Strength

0.2% offset (MPa)

Tensile strength

(MPa)

Elongation

In 5.65 √A (%)

AZ31B-O

0.5 – 1.512522110
1.5 – 6.31052219
6.3 - 751052218

AZ31B-H24

0.5 – 6.32002695
6.3 -9.51792627
9.5 – 12.71652558
12.7 - 251522488
25- 501382346
50 - 801242347

AZ31B-H26

6.3 - 101862696
10 – 12.51792626
12.5 - 201722555
20 – 251592555
25 - 401522415
40 - 501482415

The sheet and plate shall conform to the tensile requirements in above Table unless other agreement is made between seller and purchaser. Mechanical Properties for sizes and tempers not shown in above Table shall be as agreed upon by seller and purchaser.

OTHER PROPERTIES

Typical Hadness

O temper: 67 Rockwell E;

H24 temper: 83 Rockwell E

WELDABILITY

Excellent weldability with gas shielded arc using AZ61A (preferred) or AZ92A filler rod; post weld stress relief is required to prevent stress corrosion cracking. Resistance welding is excellent.

MACHINING

AZ31B, like all magnesium alloy sheet and plate, machines faster than any other metal. Providing the geometry of the part allows, the limiting factor is the power and speed of the machine rather than the quality of the tool material. The power required per cubic centimeter of metal removed varies from 9 to 14 watts per minute depending on machining operation.

Impact Energy 0.34 JImpact Energy 0.62 JImpact Energy 1.25 J
AZ21B-H24

6061 – T6

3003 – H14

5052 – H34

2024 – T6

SAE 1010 Mild Steel

0.66

0.94

2.24

1.55

0.99

1.09

1.42

1.52

3.23

2.41

1.52

1.70

2.34

2.46

4.90

3.35

2.29

2.67

.

Packaging Detail:wooden cases or as customer's requirements
Delivery Detail:within 15-25days