Utilizing the high strength properties of BISPLATE80 allows reduction in section thickness without loss of structural integrity. The following lists some applications where the strength advantage has been realized:
Induced draft fans
BISPLATE80 is a high strength steel manufactured with a controlled carbon equivalent for optimum weldability.
BISPLATE80 can be successfully welded to itself and a range of other steels, provide low hydrogen consumables are used and attention is paid to preheat, inter pass temperature, heat input and the degree of joint restraint. Stress relieving can be achieved at 540°C-570°C. Heating above this temperature should be avoided to minimize any adverse effects on mechanical properties. Cold forming can be successfully conducted, provided due account is taken of the increased strength of the steel.
|0.2% Proof Stress||690 MPa (Min)||750 MPa|
|Tensile Strength||790-930 MPa||830 MPa|
|Elongation in 50mm G.L.||18% (Min)||26%|
|Charpy Impact(Longitudinal) -20°C(10mm×10mm)||40J (Min)||160J|